One-components Epoxy Adhesives
|
|
#2423 Curing Condition:80 /45min. Tensile strength:471 kg-cm2 Bonding strength:140 kg-cm2 Paste,Super Low Temperature curing.General bonding.
|
| |
|
One-components Epoxy Adhesives
|
|
|
#2323 Curing Condition:100 /45min. Tensile strength:491 kg-cm2 Bonding strength:120 kg-cm2 Paste.Low temperature curing.Low cost.General bonding.
|
| |
|
One-components Epoxy Adhesives
|
|
|
#2223 Curing Condition:100 /45min. Tensile strength:464 kg-cm2 Bonding strength:140 kg-cm2 Liquid,Low Temperature Curing,general bonding.
|
|
|
|
One-components Epoxy Adhesives
|
|
|
#2300 Curing Condition:120 /60min. Tensile strength:450 kg-cm2 Bonding strength:120 kg-cm2 Paste,Lustering.Low Cost.For general bonding/sealing.
|
| |
|
One-components Epoxy Adhesives
|
|
|
#2200 Curing Condition:120 /60min. Tensile strength:454 kg-cm2 Bonding strength:120 kg-cm2 Liquid,Lustering for general bonding/sealing
|
| |
|
Putty & Clay Sedies
|
|
|
#S-1 Mixing ratio: 10:1 Working time: 40min. Curing time: 4hrs. Characteristics: Paste with stainless steel powder for detail crack repair. Applications: For coating/repairing/bonding of ferrous mate
|
|
|
|
Putty & Clay Sedies
|
|
|
#Plastic wood Mixing ratio: 1:1 Working time:60min. Curing time:5hrs. Characteristics: Light.Waterproof.Can be made into any shape. Functions and processed like wood. Applications: As material for CN
|
| |
|
Putty & Clay Sedies
|
|
|
#S-1 Mixing ratio: 10:1 Working time: 40min. Curing time: 4hrs. Characteristics: Paste with stainless steel powder for detail crack repair. Applications: For coating/repairing/bonding of ferrous mate
|
| |
|
Putty & Clay Sedies
|
|
|
#9900 Mixing ratio: 1:1 Working time: 60min. Curing time: 5hrs. Characteristics: Standard type.Putty.No residue on hand. Self life: 5years. Applications: For all kinds of repair, balance of motors an
|
|